干粉砂漿已經得到普及，但(dan)在(zai)應用中還存在(zai)著問題(ti)，本(ben)文從(cong)標準、生(sheng)產、配比和(he)使用中存在(zai)的問題(ti)對瓷(ci)磚粘結劑和(he)填縫(feng)劑進(jin)行分(fen)析。

一、瓷磚粘結劑

1.瓷磚(zhuan)粘結(jie)劑的執行標準

目前(qian)瓷(ci)(ci)磚粘(zhan)結(jie)劑的產品JC/T547-2005《陶(tao)瓷(ci)(ci)墻地(di)磚膠粘(zhan)劑》標(biao)準(zhun)，該標(biao)準(zhun)采(cai)用了歐洲(zhou)(zhou)的試(shi)驗方法和技術指標(biao)。但由于混凝(ning)土底(di)板、拉拔試(shi)驗及(ji)試(shi)驗用瓷(ci)(ci)磚與歐洲(zhou)(zhou)存(cun)在差(cha)距(ju)，特別是混凝(ning)土底(di)板，不同的檢(jian)(jian)(jian)驗機(ji)構之間(jian)差(cha)異比(bi)較大，造成檢(jian)(jian)(jian)驗結(jie)果(guo)可(ke)比(bi)性差(cha)，目前(qian)產品檢(jian)(jian)(jian)驗合格率(lv)比(bi)較低，有(you)產品質量(liang)的原因，同時與檢(jian)(jian)(jian)驗的不確定性有(you)很大的關系(xi)。

瓷磚(zhuan)(zhuan)施(shi)工(gong)(gong)后的(de)驗收標(biao)(biao)(biao)準(zhun)(zhun)有(you)《建筑工(gong)(gong)程飾面(mian)(mian)磚(zhuan)(zhuan)粘結強度檢驗標(biao)(biao)(biao)準(zhun)(zhun)》（JGJ110）和(he)《外墻飾面(mian)(mian)磚(zhuan)(zhuan)工(gong)(gong)程施(shi)工(gong)(gong)及驗收規(gui)程》（JGJ126）.由于產品標(biao)(biao)(biao)準(zhun)(zhun)和(he)驗收標(biao)(biao)(biao)準(zhun)(zhun)出自兩個(ge)不同的(de)管理部門，導致目前出現(xian)了一種(zhong)新(xin)情況，有(you)的(de)瓷磚(zhuan)(zhuan)粘結劑(ji)不能(neng)符合JC/T547-2005產品標(biao)(biao)(biao)準(zhun)(zhun)，但確能(neng)符合JGJ110和(he) JGJ126施(shi)工(gong)(gong)驗收標(biao)(biao)(biao)準(zhun)(zhun)。

2.瓷磚脫落(luo)原因分(fen)析

瓷(ci)磚脫落(luo)的原(yuan)因(yin)比較(jiao)多，當瓷(ci)磚出(chu)現脫落(luo)或空鼓時通常認為是粘結強度(du)低(di)。個(ge)人認為瓷(ci)磚脫落(luo)主(zhu)要有以下(xia)幾方面原(yuan)因(yin)：

1）、粘結不牢固

目(mu)前在(zai)瓷(ci)磚(zhuan)市場上，磚(zhuan)越做越大，大的(de)瓷(ci)磚(zhuan)容易(yi)下垂，傳(chuan)統(tong)的(de)瓷(ci)磚(zhuan)粘(zhan)結(jie)(jie)一般不考(kao)慮下垂性能，瓷(ci)磚(zhuan)靠自身重量的(de)下垂會(hui)大大降低粘(zhan)結(jie)(jie)強(qiang)度，目(mu)前粘(zhan)結(jie)(jie)瓷(ci)磚(zhuan)通常采(cai)用背(bei)粘(zhan)法，是(shi)在(zai)瓷(ci)磚(zhuan)背(bei)面(mian)涂粘(zhan)結(jie)(jie)劑，然后(hou)壓到(dao)墻面(mian)上，通過用橡皮錘(chui)敲打將(jiang)瓷(ci)磚(zhuan)找平，由(you)于瓷(ci)磚(zhuan)的(de)面(mian)積比較大，很難將(jiang)水泥砂漿(jiang)粘(zhan)結(jie)(jie)層的(de)空氣全部排除，這樣就容易(yi)形成空鼓，粘(zhan)結(jie)(jie)不牢固(gu)。

2）、瓷磚(zhuan)的吸水率比較低(di)

表(biao)面光滑，吸水率過(guo)低的(de)(de)瓷(ci)磚，粘(zhan)(zhan)結起來(lai)比較困難，傳統的(de)(de)瓷(ci)磚粘(zhan)(zhan)結劑(ji)已經不能(neng)符合要求，也就(jiu)是(shi)說目前市場上銷售的(de)(de)瓷(ci)磚與過(guo)去(qu)的(de)(de)瓷(ci)磚發(fa)生(sheng)了(le)非常大的(de)(de)變化，而我(wo)們采用(yong)的(de)(de)粘(zhan)(zhan)結劑(ji)和施工方法卻沒有(you)提高(gao)。

3）、瓷磚勾縫質量差

在(zai)(zai)以(yi)前的(de)填(tian)縫中，很多(duo)裝(zhuang)修隊(dui)伍都用白(bai)水(shui)(shui)泥填(tian)縫。白(bai)水(shui)(shui)泥的(de)穩定(ding)性不強，開始的(de)時候感覺還(huan)可以(yi)，但是(shi)(shi)時間(jian)長了以(yi)后(hou)就(jiu)(jiu)會出(chu)現漏縫即填(tian)縫劑與瓷(ci)(ci)(ci)磚側(ce)面粘(zhan)結(jie)不牢固的(de)情況，還(huan)有就(jiu)(jiu)是(shi)(shi)在(zai)(zai)陰濕(shi)的(de)地方會變色，（長黑(hei)綠色的(de)毛）再有就(jiu)(jiu)是(shi)(shi)水(shui)(shui)泥是(shi)(shi)吸(xi)水(shui)(shui)的(de)，它還(huan)會吸(xi)一些臟的(de)東西反(fan)應在(zai)(zai)瓷(ci)(ci)(ci)磚的(de)內(nei)側(ce)，造成變色。瓷(ci)(ci)(ci)磚的(de)縫隙開裂后(hou)水(shui)(shui)就(jiu)(jiu)要涉入，如(ru)果是(shi)(shi)外(wai)墻水(shui)(shui)進入瓷(ci)(ci)(ci)磚的(de)背(bei)面，冬(dong)季水(shui)(shui)就(jiu)(jiu)要結(jie)冰，冰的(de)體積又比水(shui)(shui)大就(jiu)(jiu)要膨脹，氣(qi)溫(wen)回(hui)升后(hou)，冰就(jiu)(jiu)要融化，這樣(yang)瓷(ci)(ci)(ci)磚非常容易脫落(luo)，我們(men)經常看到脫落(luo)后(hou)的(de)瓷(ci)(ci)(ci)磚在(zai)(zai)瓷(ci)(ci)(ci)磚背(bei)面沒有砂(sha)漿，就(jiu)(jiu)是(shi)(shi)這個(ge)道理。如(ru)果是(shi)(shi)室內(nei)的(de)瓷(ci)(ci)(ci)磚進水(shui)(shui)，由于室內(nei)的(de)廚(chu)衛間(jian)比較潮(chao)(chao)濕(shi)，且經常遇水(shui)(shui)，則水(shui)(shui)很難揮(hui)發，瓷(ci)(ci)(ci)磚粘(zhan)接(jie)層在(zai)(zai)長期潮(chao)(chao)濕(shi)環境下會大大降低粘(zhan)結(jie)強度，時間(jian)一長瓷(ci)(ci)(ci)磚脫落(luo)也就(jiu)(jiu)能(neng)理解了。

4）、瓷(ci)磚無縫鋪貼的影響

無縫本來就違背了瓷磚(zhuan)的正常使用原則(ze)。瓷磚(zhuan)本來就應(ying)該有縫隙。墻體或瓷磚(zhuan)都會出現熱變形的情(qing)況。如果無縫粘貼(tie)會使磚(zhuan)相互(hu)擠壓(ya)造(zao)成掉瓷掉角的情(qing)況甚至脫落。

以上是(shi)從(cong)材料、施(shi)工工藝(yi)等(deng)方(fang)面(mian)進(jin)行分析瓷磚(zhuan)脫(tuo)(tuo)落(luo)的(de)原因，不涉及產(chan)品(pin)質(zhi)量、施(shi)工環境和工人(ren)施(shi)工水平等(deng)因素。總之，造成(cheng)瓷磚(zhuan)脫(tuo)(tuo)落(luo)的(de)原因非常復雜，但只要正確(que)選用瓷磚(zhuan)粘結劑和合理的(de)施(shi)工工藝(yi)才是(shi)保證工程質(zhi)量的(de)前提。

3.薄層(ceng)法施工(gong)存在的(de)問題

50多年前，羅斯伯(bo)格(ge)博士(shi)發(fa)明(ming)了(le)瓷磚(zhuan)(zhuan)和(he)(he)石(shi)(shi)材(cai)的(de)(de)(de)薄床施(shi)工(gong)(gong)(gong)技(ji)術（亦稱為鏝(man)刀法），徹底改(gai)變了(le)傳統的(de)(de)(de)磚(zhuan)(zhuan)石(shi)(shi)安裝方法，給磚(zhuan)(zhuan)石(shi)(shi)施(shi)工(gong)(gong)(gong)領域(yu)帶來了(le)一次革命。這(zhe)種施(shi)工(gong)(gong)(gong)方法既能保證磚(zhuan)(zhuan)石(shi)(shi)安裝的(de)(de)(de)牢固和(he)(he)耐久，同時對施(shi)工(gong)(gong)(gong)人員(yuan)勞動熟練程度要求不高(gao)，這(zhe)正適(shi)應于目前國(guo)內(nei)磚(zhuan)(zhuan)石(shi)(shi)消費升級和(he)(he)技(ji)工(gong)(gong)(gong)短(duan)缺的(de)(de)(de)現實。50多年來世界各(ge)地的(de)(de)(de)砂漿(jiang)企業不斷推出新的(de)(de)(de)產(chan)品和(he)(he)技(ji)術，應用于瓷磚(zhuan)(zhuan)和(he)(he)石(shi)(shi)材(cai)的(de)(de)(de)施(shi)工(gong)(gong)(gong)中。這(zhe)些系列產(chan)品進入(ru)中國(guo)已有10年的(de)(de)(de)歷史，應用于國(guo)內(nei)許多知名工(gong)(gong)(gong)程，但一直沒有得到令人滿意(yi)(yi)的(de)(de)(de)推廣。愿意(yi)(yi)如下：

1）、表現價格高。

許(xu)多用(yong)戶(hu)不比(bi)質量只(zhi)比(bi)價格(ge)；只(zhi)比(bi)單價不比(bi)用(yong)量；只(zhi)比(bi)單價不比(bi)綜合成(cheng)本；給干粉瓷磚粘結劑的(de)推廣造成(cheng)麻煩(fan)。

2）、與傳統(tong)施工工藝有沖突，施工工人不(bu)會使用。

厚(hou)層粘結（背粘法(fa)）普遍應用(yong)(yong)的(de)原因(yin)之一是粘結基層表面(mian)的(de)平(ping)整度和(he)垂直度比(bi)較(jiao)差，厚(hou)層粘結不(bu)僅起粘結的(de)作用(yong)(yong)更重要的(de)是基層找平(ping)（通常厚(hou)層粘結的(de)砂漿在1-3厘米），在基層平(ping)整比(bi)較(jiao)差時(shi)時(shi)不(bu)能采(cai)用(yong)(yong)薄層施(shi)(shi)工(gong)。曾(ceng)經有些生產企業免費給施(shi)(shi)工(gong)人(ren)員(yuan)(yuan)提供齒(chi)形鏝刀，但施(shi)(shi)工(gong)人(ren)員(yuan)(yuan)依舊不(bu)采(cai)用(yong)(yong)，主要一個(ge)原因(yin)是基層的(de)平(ping)整達不(bu)到要求(qiu)，需要增(zeng)加一次(ci)找平(ping)的(de)施(shi)(shi)工(gong)工(gong)藝，工(gong)人(ren)認(ren)為(wei)(wei)麻煩。個(ge)人(ren)認(ren)為(wei)(wei)薄法(fa)施(shi)(shi)工(gong)技(ji)術推(tui)廣的(de)關(guan)鍵是對施(shi)(shi)工(gong)工(gong)人(ren)進(jin)行技(ji)術培訓。

3）、宣(xuan)傳、推(tui)廣(guang)力度不(bu)夠

目前許多施(shi)(shi)工(gong)(gong)(gong)工(gong)(gong)(gong)人對(dui)薄層法(fa)（鏝(man)刀法(fa)）不(bu)了解，更談(tan)不(bu)上應用，薄層法(fa)施(shi)(shi)工(gong)(gong)(gong)工(gong)(gong)(gong)人接受(shou)起來(lai)比較困難，理論(lun)上鏝(man)刀法(fa)的(de)(de)施(shi)(shi)工(gong)(gong)(gong)速(su)度(du)(du)比傳統的(de)(de)施(shi)(shi)工(gong)(gong)(gong)方法(fa)提高很多，但由于(yu)工(gong)(gong)(gong)人的(de)(de)接受(shou)程(cheng)度(du)(du)及增加基層預(yu)先處(chu)理環節（）包(bao)括熟練(lian)程(cheng)度(du)(du)，導致用鏝(man)刀法(fa)的(de)(de)施(shi)(shi)工(gong)(gong)(gong)速(su)度(du)(du)反(fan)而低。北(bei)京某施(shi)(shi)工(gong)(gong)(gong)公(gong)司(si)對(dui)施(shi)(shi)工(gong)(gong)(gong)工(gong)(gong)(gong)人經過(guo)培訓后(hou)，其完全掌握薄法(fa)施(shi)(shi)工(gong)(gong)(gong)技能，從(cong)而大幅(fu)度(du)(du)提高工(gong)(gong)(gong)效，在目前瓦工(gong)(gong)(gong)工(gong)(gong)(gong)價飆漲的(de)(de)情(qing)況下，施(shi)(shi)工(gong)(gong)(gong)的(de)(de)綜合(he)成本更低，由于(yu)鋪貼的(de)(de)堅固和耐久，收到(dao)客戶廣(guang)泛的(de)(de)好評。業務(wu)來(lai)源不(bu)斷(duan)增加，公(gong)司(si)得到(dao)了良(liang)好的(de)(de)收益。

4.瓷磚粘結劑(ji)的配(pei)方

瓷(ci)磚(zhuan)粘(zhan)結(jie)劑(ji)(ji)(ji)目前(qian)實際使(shi)用(yong)與檢驗(yan)嚴重脫節(jie)，JC/T547-2004標準主要是(shi)針對薄(bo)層(ceng)施工(gong)(gong)法(fa)(fa)而(er)制訂，目前(qian)在我國瓷(ci)磚(zhuan)薄(bo)貼(tie)法(fa)(fa)（鏝刀法(fa)(fa)）施工(gong)(gong)尚不普及，更(geng)多(duo)的(de)(de)(de)(de)是(shi)采用(yong)背粘(zhan)法(fa)(fa)，如(ru)果(guo)用(yong)薄(bo)貼(tie)法(fa)(fa)的(de)(de)(de)(de)瓷(ci)磚(zhuan)粘(zhan)結(jie)劑(ji)(ji)(ji)進(jin)行厚(hou)層(ceng)粘(zhan)貼(tie)，會(hui)出現(xian)一些(xie)問題，厚(hou)貼(tie)法(fa)(fa)的(de)(de)(de)(de)瓷(ci)磚(zhuan)粘(zhan)結(jie)劑(ji)(ji)(ji)也(ye)不能(neng)用(yong)于(yu)(yu)鏝刀法(fa)(fa)施工(gong)(gong)，鏝刀法(fa)(fa)施工(gong)(gong)的(de)(de)(de)(de)瓷(ci)磚(zhuan)粘(zhan)結(jie)劑(ji)(ji)(ji)，由于(yu)(yu)施工(gong)(gong)厚(hou)度薄(bo)，所以需要有(you)良好(hao)的(de)(de)(de)(de)保(bao)水性，纖維(wei)素醚的(de)(de)(de)(de)用(yong)量(liang)要增加，而(er)背貼(tie)法(fa)(fa)由于(yu)(yu)粘(zhan)結(jie)層(ceng)比較厚(hou)，纖維(wei)素醚的(de)(de)(de)(de)用(yong)量(liang)不宜過(guo)多(duo)，否(fou)則影響粘(zhan)結(jie)層(ceng)的(de)(de)(de)(de)固(gu)化(hua)。

5.瓷磚粘結劑的(de)類型

隨著(zhu)干粉砂漿的(de)普及推廣，干粉砂漿的(de)使用(yong)(yong)越來越普遍，目(mu)前(qian)市場上的(de)瓷(ci)磚粘結(jie)(jie)劑主要有以(yi)下幾種(zhong)：1）用(yong)(yong)于大(da)(da)(da)理石、文化石等石材(cai)或大(da)(da)(da)型(xing)瓷(ci)磚粘結(jie)(jie)；2）用(yong)(yong)于外保溫上（基層變形大(da)(da)(da)）貼瓷(ci)磚或一(yi)些吸水率比較小(xiao)的(de)瓷(ci)磚粘結(jie)(jie)；3）用(yong)(yong)于普通瓷(ci)磚的(de)粘結(jie)(jie)；4）用(yong)(yong)于地面瓷(ci)磚的(de)粘結(jie)(jie)。

目(mu)(mu)前，地(di)(di)(di)面(mian)(mian)(mian)瓷(ci)磚(zhuan)(zhuan)粘(zhan)(zhan)結(jie)(jie)劑(ji)(ji)的(de)(de)(de)(de)推廣使用(yong)存(cun)在許(xu)多問(wen)(wen)題，首先是施工(gong)條件，國外的(de)(de)(de)(de)地(di)(di)(di)面(mian)(mian)(mian)瓷(ci)磚(zhuan)(zhuan)粘(zhan)(zhan)貼時，基層的(de)(de)(de)(de)平整(zheng)度比較好，因(yin)(yin)此也可以(yi)(yi)采用(yong)鏝刀法施工(gong)，國內目(mu)(mu)前的(de)(de)(de)(de)地(di)(di)(di)面(mian)(mian)(mian)平整(zheng)度非常差，更(geng)多的(de)(de)(de)(de)是一(yi)次(ci)結(jie)(jie)構的(de)(de)(de)(de)基礎，誤(wu)差非常大。其(qi)次(ci)是標(biao)準(zhun)問(wen)(wen)題，JC/T547標(biao)準(zhun)名稱是為陶瓷(ci)墻(qiang)地(di)(di)(di)磚(zhuan)(zhuan)粘(zhan)(zhan)結(jie)(jie)劑(ji)(ji)，已經(jing)包括地(di)(di)(di)面(mian)(mian)(mian)的(de)(de)(de)(de)瓷(ci)磚(zhuan)(zhuan)粘(zhan)(zhan)結(jie)(jie)劑(ji)(ji)，如果按標(biao)準(zhun)生(sheng)產則成(cheng)本(ben)過(guo)高(gao)，過(guo)去傳統的(de)(de)(de)(de)墻(qiang)面(mian)(mian)(mian)瓷(ci)磚(zhuan)(zhuan)粘(zhan)(zhan)結(jie)(jie)劑(ji)(ji)水(shui)泥用(yong)量(liang)比較大，而(er)且還有(you)加入一(yi)定(ding)量(liang)的(de)(de)(de)(de)液體(ti)膠(jiao)(jiao)，有(you)一(yi)定(ding)的(de)(de)(de)(de)成(cheng)本(ben)，而(er)地(di)(di)(di)磚(zhuan)(zhuan)粘(zhan)(zhan)結(jie)(jie)采用(yong)干鋪法，水(shui)泥用(yong)量(liang)比較少(shao)，也不需要加膠(jiao)(jiao)，所以(yi)(yi)成(cheng)本(ben)更(geng)低(di)。另(ling)一(yi)個原因(yin)(yin)是目(mu)(mu)前地(di)(di)(di)磚(zhuan)(zhuan)粘(zhan)(zhan)結(jie)(jie)砂漿的(de)(de)(de)(de)厚(hou)度至少(shao)在3厘米(mi)以(yi)(yi)上(shang)。最(zui)后是觀念問(wen)(wen)題，通常人們認為地(di)(di)(di)面(mian)(mian)(mian)的(de)(de)(de)(de)瓷(ci)磚(zhuan)(zhuan)粘(zhan)(zhan)貼對粘(zhan)(zhan)結(jie)(jie)強度要求不高(gao)，即便粘(zhan)(zhan)結(jie)(jie)不牢固(gu)最(zui)多也就是空鼓(gu)，不會因(yin)(yin)脫落造成(cheng)工(gong)程(cheng)質量(liang)事故。

二、瓷磚填縫劑

1.瓷磚填縫(feng)劑的作用

瓷(ci)磚(zhuan)(zhuan)填縫(feng)劑(ji)目前已經得到了普(pu)及，推廣(guang)和使用情(qing)況比瓷(ci)磚(zhuan)(zhuan)粘結(jie)劑(ji)好，瓷(ci)磚(zhuan)(zhuan)填縫(feng)劑(ji)不僅使用方便，而且有不同的顏色(se)可以選擇，與瓷(ci)磚(zhuan)(zhuan)的整體(ti)效果好。通過標準可以看出，瓷(ci)磚(zhuan)(zhuan)填縫(feng)劑(ji)對吸水量(liang)有要(yao)求(qiu)(qiu)，也就是(shi)要(yao)求(qiu)(qiu)填縫(feng)劑(ji)具有一定的防水性，可以防止水從瓷(ci)磚(zhuan)(zhuan)的縫(feng)隙(xi)之間滲入瓷(ci)磚(zhuan)(zhuan)內(nei)部，避免瓷(ci)磚(zhuan)(zhuan)脫(tuo)落和墻體(ti)森誰發霉。

2.瓷磚(zhuan)填縫(feng)劑的配方(fang)

瓷磚填縫劑的配方主要從以下幾方面考(kao)慮：

1） 根(gen)據瓷磚(zhuan)的縫隙確定。

常將瓷(ci)磚(zhuan)的縫(feng)(feng)隙(xi)(xi)分(fen)(fen)為兩(liang)種，寬(kuan)縫(feng)(feng)和(he)窄縫(feng)(feng)，寬(kuan)縫(feng)(feng)指大于5mm的縫(feng)(feng)隙(xi)(xi)；窄縫(feng)(feng)指5mm以下的縫(feng)(feng)隙(xi)(xi)。也可以分(fen)(fen)為有(you)砂(sha)型和(he)無砂(sha)型，有(you)砂(sha)型用于5mm以上的縫(feng)(feng)隙(xi)(xi)，無砂(sha)型用于5mm以下的縫(feng)(feng)隙(xi)(xi)。總之，瓷(ci)磚(zhuan)填縫(feng)(feng)劑配方中的砂(sha)的比例和(he)粒徑需(xu)要按照瓷(ci)磚(zhuan)的縫(feng)(feng)隙(xi)(xi)確定。

2） 根據(ju)顏色確定

如果是(shi)白色或淺色的(de)(de)(de)瓷磚填縫劑，基(ji)本不(bu)需要(yao)考慮(lv)泛堿(jian)(jian)問題(ti)，而黑(hei)色或深色（紅色、棕色）的(de)(de)(de)填縫劑則必須(xu)考慮(lv)泛堿(jian)(jian)問題(ti)，水泥基(ji)材料只要(yao)在一定溫度和(he)濕(shi)度的(de)(de)(de)情況下(xia)泛堿(jian)(jian)是(shi)一個不(bu)可(ke)避免的(de)(de)(de)問題(ti)，通過反復試驗，認(ren)為加入阻堿(jian)(jian)劑的(de)(de)(de)效果最好，盡管(guan)不(bu)能從(cong)根本上解決泛堿(jian)(jian)，但(dan)相(xiang)比其他方法是(shi)最有效的(de)(de)(de)。

3.瓷(ci)磚填縫劑的容易出現的問題

1）強度(du)不(bu)夠。特別是白色的(de)瓷磚(zhuan)填縫劑，一些單位為了追求白度(du)，減少水硬性材(cai)料的(de)用量，甚(shen)至取消，導致白度(du)提(ti)高了，但強度(du)大大減低，出現(xian)(xian)表面脫粉，遇(yu)水軟化現(xian)(xian)象。

2）泛(fan)(fan)堿(jian)(jian)。前(qian)面已經講過泛(fan)(fan)堿(jian)(jian)的(de)原因(yin)和解決的(de)方法，泛(fan)(fan)堿(jian)(jian)并不是所有(you)的(de)深色填縫劑(ji)都泛(fan)(fan)堿(jian)(jian)，目前(qian)許多人更(geng)多的(de)是抱(bao)有(you)僥(jiao)幸心理，萬一不泛(fan)(fan)堿(jian)(jian)就可以(yi)降低成(cheng)本。同(tong)時瓷(ci)磚粘結(jie)劑(ji)的(de)質(zhi)量不好也會造成(cheng)泛(fan)(fan)堿(jian)(jian)，特別是陶質(zhi)磚和薄層(ceng)石材。

3）開(kai)裂。瓷(ci)磚填縫劑開(kai)裂目前尚(shang)未一(yi)起重視，表面(mian)上(shang)僅僅是美觀，短期內不(bu)會(hui)影響質(zhi)量，但水可以通過開(kai)裂的縫隙滲入，隨著時間的推(tui)移，質(zhi)量問題就要出現，我(wo)們(men)通常看到瓷(ci)磚的脫落會(hui)在一(yi)年以后發生這(zhe)也(ye)是其中原(yuan)因之一(yi)。

4.瓷磚填(tian)縫劑的使用注意事項

1）瓷(ci)磚粘貼至少在24小時后(hou)進行填縫(feng)，填縫(feng)的時間間隔(ge)越長(chang)越好，使瓷(ci)磚粘結的水分排(pai)除(chu)，減少泛堿(jian)。

2）陶質(zhi)或麻面瓷磚(zhuan)施工(gong)前應先用水提前濕潤(run)，便于勾(gou)縫后清洗(xi)。

3）施工后保證嵌縫材料24小時內不受(shou)水沖洗。

本文來自: 中國砂漿網(//www.mortar.cn/) 詳細(xi)出處參考：//www.mortar.cn/sjz/yfpf/2011/0726/43566.html